S650MC cold forming automobile steel

Pricing: Request an order-specific quote

Reference: S650MC cold forming automobile steel. Check the form, thickness and approved fabrication route for the order.

Processing: Specify drawing requirements with your enquiry.

Available dimensions: Confirm by grade, form and quantity on quote.

E-mail: [email protected]

Whatsapp: +86-18272866905

Chat Online Leave a Message

S650MC cold forming automobile steel Description

S650MC cold forming automobile steel. Use the approved fabrication procedure for the actual thickness, delivery condition and joint or part geometry.

Specify plate, sheet or coil, thickness, forming direction, bend requirements, surface condition and the project approval process.

Supply dimensions, lead time and inspection are confirmed against the order and mill offer.

S650MC automotive steel is a high-strength, high-durability automotive steel. Its main feature is that S650MC steel has good impact and compression resistance, which can ensure that the structural parts of the car will not be damaged due to structural damage during impact, and ensure the safety and reliability of the car. S650MC hot-rolled steel has good corrosion resistance, which can effectively prevent the structural parts of the car from being corroded, thereby prolonging the service life of the car.

S650MC automotive structural steel is a low carbon steel with good antistatic properties, good plasticity and toughness, can withstand high temperature treatment, and has good welding properties. S650MC automotive steel can be used in the production of automotive suspensions to withstand the greater impact generated by various vehicles during driving, thereby ensuring the stability and durability of axles, wheels and engine brackets.

EN10149-2 S650MC automotive steel has excellent stamping performance, can resist recoil force, tension force and torsion force, and can withstand the large impact produced by the car at high speed. In addition, it has good impact plasticity and can resist the impact force exerted by road conditions on automotive structural parts. S650MC steel has good tensile strength and elastic modulus, which can meet various loading requirements of axles, wheels and engine mounts.

S650MC cold forming automobile steel Datasheet

Legacy technical note · verification required

Size: Thickness from 1.5mm-16mm
width from 900mm-1850mm
length from 1m-12m or according to customer's special request
Standard: EN 10149-2
Size Tolerance: ±1%-3%
Processing method: Bending, Welding, Decoiling, Cutting, Punching, Polishing or as customer's request
Technology: Hot roll, cold roll, cold drawn, ect.
Weight Calculation: Weight(kg)=Thickness(mm)*Width(m)*Length(m)*Density(7.85g/cm3)
Trade Term: FOB,CIF,CFR,EXW,etc.
MOQ: 10tons. We also can accept sample order.

S650MC cold forming automobile steel Chemical composition

Legacy technical table · verification required

Confirm every value against the applicable edition, thickness and material certificate.

Legacy technical table
EN 10149-2	C	Si	Mn	P	S	Nb	V	Ti	Al	Mo	B
S650MC	0.12	0.60	2.0	0.025	0.015	0.09	0.2	0.22	0.015	0.5	0.005

S650MC cold forming automobile steel Mechanical Properties

Legacy technical table · verification required

Confirm every value against the applicable edition, thickness and material certificate.

Legacy technical table
EN 10149-2	Yield Strength	Tensile Strength	Elongation
EN 10149-2	Yield Strength	Tensile Strength	t<3mm	t≥3mm
S650MC	≥ 650 Mpa	700-880 Mpa	10%	12%

Equivalent Grade of S650MC cold forming automobile steel

Legacy technical table · verification required

Confirm every value against the applicable edition, thickness and material certificate.

Legacy technical table
EN	Germany
EN	DIN,WNr
S650MC	1.0989
S650MC	QStE650TM

Source and scope

DIN EN 10149-2:2013-12 · Scope, Tables 1–2 and delivery condition 7.2. Part 2 concerns thermomechanically rolled high-yield flat products for cold forming. The grade and thickness determine the applicable property row.

Apply the cited scope to the matching designation and form. Confirm any remaining technical values with the applicable edition or material certificate.